DETAILS
Production procedure:
Raw elements (C, Fe, Ni, Mn, Cr and Cu), smelted into ingots by AOD finery, hot rolled into black surface, pickling into acid liquid, polished by automatically machine and cutting into pieces
Standards:
ASTM A276, A484, A564, A581, A582, EN 10272, JIS4303, JIS G 431, JIS G 4311 and JIS G 4318
| Grade | Chemical Component % | |||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Other | ||
| 316 | 0Cr17Ni12Mo2 | ≤0.08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - |
| 316L | 00Cr17Ni14Mo2 | ≤0.030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - |
| 316N | 0Cr17Ni12Mo2N | ≤0.08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.10-0.22 | - |
| 316Ti | 00Cr17Ni13Mo2N | ≤0.080 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | |
| 316J1 | 0Cr18Ni12Mo2Cu2 | ≤0.08 | 17.00-19.00 | 10.00-14.50 | ≤2.00 | ≤0.035 | ≤0.030 | 1.20-2.75 | ≤1.00 | 1.00-2.50 | - | - |
| 316J1L | 00Cr18Ni14Mo2Cu2 | ≤0.030 | 17.00-19.00 | 12.00-16.00 | ≤2.00 | ≤0.035 | ≤0.030 | 1.20-2.75 | ≤1.00 | 1.00-2.50 | - | - |
| 317 | 0Cr19Ni13Mo3 | ≤0.12 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.035 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | - | - |
| 317L | 00Cr19Ni13Mo3 | ≤0.08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.035 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | - | - |
| 1Cr18Ni12Mo3Ti6 | ≤0.12 | 16.00-19.00 | 11.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.50-3.50 | ≤1.00 | - | - | Ti5(C | |